Luvocom® 3F PEEK CF 9676 BK Filament is a 15% carbon reinforced PEEK (Polyether Ether Ketone) with extraordinary characteristics in terms of mechanical, thermal and chemical resistance. PEEK with carbon is used in demanding industries like oil and gas, automotive, mechanical engineering, aircraft and aerospace technologies. This particular high performance polymer grade is tailored made for the 3D printing industry to match the injection molding strength requirements and focusing on the serial production of end-parts. This 3D4Makers PEEK CF filament features the following properties:
Excellent mechanical, thermal and chemical performance
Suitable for demanding industrial applications
Inherent flame retardant
High dimensional stability
Material properties
| Description | Value | Test method |
|---|---|---|
| Density | 1,36 g/cm3 | ISO 1183 |
| Tensile strength (at 23°C/50% rh) | 126 MPa | ISO 527 |
| Elongation (at 23°C/50% rh) |
3,9 %
|
ISO 527 |
| Modulus of Elasticity (at 23°C/50% rh) | 7,8 GPa | ISO 527 |
| Charpy Impact Strength | 66 kJ/m² | eU |
| Charpy Impact Strength notched | 7 kJ/m² | |
| Heat Distortion Temp (HDT A) | 280 °C | ISO 75 |
| Continuous Service Temp. | 250 °C | UL 746B |
| Maximum (short term) Use Temp. | 280 °C | / |
| Insulation Resistance (Strip electrode R25) | <10⁹ Ω | DIN/IEC 60167 |
| Surface Resistance | <10⁹ Ω | DIN IEC 60093 |
Printer recommendations
| Description | Value |
|---|---|
| Printer nozzle temperature | 400 - 450°C |
| Heated bed temperature | 110°C + |
| Print Speed | 15 - 30 mm/s |
| Bed Adhesion | Magigoo HT on glass or a PEI Sheet |
| Pre drying recommendations | 120°C, 4 - 8 hours |
To get the best results while printing we advise you to keep the 3D printer in a room where there is hardly any draft and/or temperature fluctuations. When the 3D printer is not being used it is important to keep filament in a bag and stored in a cool, dry and dark place until it is used again.
Luvocom® 3F PEEK CF 9676 BK Filament is a 15% carbon reinforced PEEK (Polyether Ether Ketone) with extraordinary characteristics in terms of mechanical, thermal and chemical resistance. PEEK with carbon is used in demanding industries like oil and gas, automotive, mechanical engineering, aircraft and aerospace technologies. This particular high performance polymer grade is tailored made for the 3D printing industry to match the injection molding strength requirements and focusing on the serial production of end-parts. This 3D4Makers PEEK CF filament features the following properties:
Excellent mechanical, thermal and chemical performance
Suitable for demanding industrial applications
Inherent flame retardant
High dimensional stability
Material properties
| Description | Value | Test method |
|---|---|---|
| Density | 1,36 g/cm3 | ISO 1183 |
| Tensile strength (at 23°C/50% rh) | 126 MPa | ISO 527 |
| Elongation (at 23°C/50% rh) |
3,9 %
|
ISO 527 |
| Modulus of Elasticity (at 23°C/50% rh) | 7,8 GPa | ISO 527 |
| Charpy Impact Strength | 66 kJ/m² | eU |
| Charpy Impact Strength notched | 7 kJ/m² | |
| Heat Distortion Temp (HDT A) | 280 °C | ISO 75 |
| Continuous Service Temp. | 250 °C | UL 746B |
| Maximum (short term) Use Temp. | 280 °C | / |
| Insulation Resistance (Strip electrode R25) | <10⁹ Ω | DIN/IEC 60167 |
| Surface Resistance | <10⁹ Ω | DIN IEC 60093 |
Printer recommendations
| Description | Value |
|---|---|
| Printer nozzle temperature | 400 - 450°C |
| Heated bed temperature | 110°C + |
| Print Speed | 15 - 30 mm/s |
| Bed Adhesion | Magigoo HT on glass or a PEI Sheet |
| Pre drying recommendations | 120°C, 4 - 8 hours |
To get the best results while printing we advise you to keep the 3D printer in a room where there is hardly any draft and/or temperature fluctuations. When the 3D printer is not being used it is important to keep filament in a bag and stored in a cool, dry and dark place until it is used again.
Luvocom® 3F PEEK CF 9676 BK Filament is a 15% carbon reinforced PEEK (Polyether Ether Ketone) with extraordinary characteristics in terms of mechanical, thermal and chemical resistance. PEEK with carbon is used in demanding industries like oil and gas, automotive, mechanical engineering, aircraft and aerospace technologies. This particular high performance polymer grade is tailored made for the 3D printing industry to match the injection molding strength requirements and focusing on the serial production of end-parts. This 3D4Makers PEEK CF filament features the following properties:
Excellent mechanical, thermal and chemical performance
Suitable for demanding industrial applications
Inherent flame retardant
High dimensional stability
Material properties
| Description | Value | Test method |
|---|---|---|
| Density | 1,36 g/cm3 | ISO 1183 |
| Tensile strength (at 23°C/50% rh) | 126 MPa | ISO 527 |
| Elongation (at 23°C/50% rh) |
3,9 %
|
ISO 527 |
| Modulus of Elasticity (at 23°C/50% rh) | 7,8 GPa | ISO 527 |
| Charpy Impact Strength | 66 kJ/m² | eU |
| Charpy Impact Strength notched | 7 kJ/m² | |
| Heat Distortion Temp (HDT A) | 280 °C | ISO 75 |
| Continuous Service Temp. | 250 °C | UL 746B |
| Maximum (short term) Use Temp. | 280 °C | / |
| Insulation Resistance (Strip electrode R25) | <10⁹ Ω | DIN/IEC 60167 |
| Surface Resistance | <10⁹ Ω | DIN IEC 60093 |
Printer recommendations
| Description | Value |
|---|---|
| Printer nozzle temperature | 400 - 450°C |
| Heated bed temperature | 110°C + |
| Print Speed | 15 - 30 mm/s |
| Bed Adhesion | Magigoo HT on glass or a PEI Sheet |
| Pre drying recommendations | 120°C, 4 - 8 hours |
To get the best results while printing we advise you to keep the 3D printer in a room where there is hardly any draft and/or temperature fluctuations. When the 3D printer is not being used it is important to keep filament in a bag and stored in a cool, dry and dark place until it is used again.
Luvocom® 3F PEEK CF 9676 BK Filament is a 15% carbon reinforced PEEK (Polyether Ether Ketone) with extraordinary characteristics in terms of mechanical, thermal and chemical resistance. PEEK with carbon is used in demanding industries like oil and gas, automotive, mechanical engineering, aircraft and aerospace technologies. This particular high performance polymer grade is tailored made for the 3D printing industry to match the injection molding strength requirements and focusing on the serial production of end-parts. This 3D4Makers PEEK CF filament features the following properties:
Excellent mechanical, thermal and chemical performance
Suitable for demanding industrial applications
Inherent flame retardant
High dimensional stability
Material properties
| Description | Value | Test method |
|---|---|---|
| Density | 1,36 g/cm3 | ISO 1183 |
| Tensile strength (at 23°C/50% rh) | 126 MPa | ISO 527 |
| Elongation (at 23°C/50% rh) |
3,9 %
|
ISO 527 |
| Modulus of Elasticity (at 23°C/50% rh) | 7,8 GPa | ISO 527 |
| Charpy Impact Strength | 66 kJ/m² | eU |
| Charpy Impact Strength notched | 7 kJ/m² | |
| Heat Distortion Temp (HDT A) | 280 °C | ISO 75 |
| Continuous Service Temp. | 250 °C | UL 746B |
| Maximum (short term) Use Temp. | 280 °C | / |
| Insulation Resistance (Strip electrode R25) | <10⁹ Ω | DIN/IEC 60167 |
| Surface Resistance | <10⁹ Ω | DIN IEC 60093 |
Printer recommendations
| Description | Value |
|---|---|
| Printer nozzle temperature | 400 - 450°C |
| Heated bed temperature | 110°C + |
| Print Speed | 15 - 30 mm/s |
| Bed Adhesion | Magigoo HT on glass or a PEI Sheet |
| Pre drying recommendations | 120°C, 4 - 8 hours |
To get the best results while printing we advise you to keep the 3D printer in a room where there is hardly any draft and/or temperature fluctuations. When the 3D printer is not being used it is important to keep filament in a bag and stored in a cool, dry and dark place until it is used again.
Luvocom® 3F PEEK CF 9676 BK Filament is a 15% carbon reinforced PEEK (Polyether Ether Ketone) with extraordinary characteristics in terms of mechanical, thermal and chemical resistance. PEEK with carbon is used in demanding industries like oil and gas, automotive, mechanical engineering, aircraft and aerospace technologies. This particular high performance polymer grade is tailored made for the 3D printing industry to match the injection molding strength requirements and focusing on the serial production of end-parts. This 3D4Makers PEEK CF filament features the following properties:
Excellent mechanical, thermal and chemical performance
Suitable for demanding industrial applications
Inherent flame retardant
High dimensional stability
Material properties
| Description | Value | Test method |
|---|---|---|
| Density | 1,36 g/cm3 | ISO 1183 |
| Tensile strength (at 23°C/50% rh) | 126 MPa | ISO 527 |
| Elongation (at 23°C/50% rh) |
3,9 %
|
ISO 527 |
| Modulus of Elasticity (at 23°C/50% rh) | 7,8 GPa | ISO 527 |
| Charpy Impact Strength | 66 kJ/m² | eU |
| Charpy Impact Strength notched | 7 kJ/m² | |
| Heat Distortion Temp (HDT A) | 280 °C | ISO 75 |
| Continuous Service Temp. | 250 °C | UL 746B |
| Maximum (short term) Use Temp. | 280 °C | / |
| Insulation Resistance (Strip electrode R25) | <10⁹ Ω | DIN/IEC 60167 |
| Surface Resistance | <10⁹ Ω | DIN IEC 60093 |
Printer recommendations
| Description | Value |
|---|---|
| Printer nozzle temperature | 400 - 450°C |
| Heated bed temperature | 110°C + |
| Print Speed | 15 - 30 mm/s |
| Bed Adhesion | Magigoo HT on glass or a PEI Sheet |
| Pre drying recommendations | 120°C, 4 - 8 hours |
To get the best results while printing we advise you to keep the 3D printer in a room where there is hardly any draft and/or temperature fluctuations. When the 3D printer is not being used it is important to keep filament in a bag and stored in a cool, dry and dark place until it is used again.
Luvocom® 3F PEEK CF 9676 BK Filament is a 15% carbon reinforced PEEK (Polyether Ether Ketone) with extraordinary characteristics in terms of mechanical, thermal and chemical resistance. PEEK with carbon is used in demanding industries like oil and gas, automotive, mechanical engineering, aircraft and aerospace technologies. This particular high performance polymer grade is tailored made for the 3D printing industry to match the injection molding strength requirements and focusing on the serial production of end-parts. This 3D4Makers PEEK CF filament features the following properties:
Excellent mechanical, thermal and chemical performance
Suitable for demanding industrial applications
Inherent flame retardant
High dimensional stability
Material properties
| Description | Value | Test method |
|---|---|---|
| Density | 1,36 g/cm3 | ISO 1183 |
| Tensile strength (at 23°C/50% rh) | 126 MPa | ISO 527 |
| Elongation (at 23°C/50% rh) |
3,9 %
|
ISO 527 |
| Modulus of Elasticity (at 23°C/50% rh) | 7,8 GPa | ISO 527 |
| Charpy Impact Strength | 66 kJ/m² | eU |
| Charpy Impact Strength notched | 7 kJ/m² | |
| Heat Distortion Temp (HDT A) | 280 °C | ISO 75 |
| Continuous Service Temp. | 250 °C | UL 746B |
| Maximum (short term) Use Temp. | 280 °C | / |
| Insulation Resistance (Strip electrode R25) | <10⁹ Ω | DIN/IEC 60167 |
| Surface Resistance | <10⁹ Ω | DIN IEC 60093 |
Printer recommendations
| Description | Value |
|---|---|
| Printer nozzle temperature | 400 - 450°C |
| Heated bed temperature | 110°C + |
| Print Speed | 15 - 30 mm/s |
| Bed Adhesion | Magigoo HT on glass or a PEI Sheet |
| Pre drying recommendations | 120°C, 4 - 8 hours |
To get the best results while printing we advise you to keep the 3D printer in a room where there is hardly any draft and/or temperature fluctuations. When the 3D printer is not being used it is important to keep filament in a bag and stored in a cool, dry and dark place until it is used again.
Contactgegevens
Maandag 09:00 - 17:00
Dinsdag 09:00 - 17:00
Woensdag 09:00 - 17:00
Donderdag 09:00 - 17:00
Vrijdag 09:00 - 17:00
OP Zaterdags GESLOTEN (eventueel op afspraak)
Zondag Gesloten
Oudeweg 91-95 Unit: A.02/0.3
MAAK Haarlem
2031 CC Haarlem
085-3037232
info@multi-3dprint.nl