COMPOSITE-X
Liqcreate Composite-X is an extremely rigid and high performance reinforced nano-micro composite resin for SLA, DLP & LCD / MSLA in the range of 385 – 420nm. Perfect for rapid tooling, wind tunnel testing and industrial applications.
Liqcreate Composite-X is one of the stiffest and strongest material available in the market. It has a flexural modulus over 9000 MPa and a flexural strength of 150 – 170 MPa. The material can be used after UV-post curing, or the properties can be boosted with a thermal cure. This material has features like excellent chemical resistance, high strength and high stiffness.
 |
 |
 |
|
High
strength
|
Nano reinforced
|
Low shrinkage
|
Polymer properties
| Mechanical Properties | Metric |
|---|
| Description | ASTM Method | UV curing 60 min. at 60°C | UV curing 60 min. at 60°C
& thermal curing 120 min. at 100°C |
|---|
| Tensile strength |
D638M |
50 – 75 MPa |
70 – 85 MPa |
| Tensile modulus |
D638M |
7.5 – 8.5 GPa |
8.5 – 9.5 GPa |
| Elongation at break |
D638M |
1% |
1% |
| Flexural strength |
D790M |
140 – 150 MPa |
150 – 170 MPa |
| Flexural modulus |
D2240 |
7.5 – 8.5 GPa |
8.5 – 9.5 GPa |
| IZOD Impact (notched) |
D256A |
19 J/m |
18 J/m |
| Shore D Hardness |
D2240 |
93 |
94 |
| Water sorption |
D570-98 |
0.67% |
0.59% |
| Linear Shrinkage during printing |
Internal method |
<0.1% |
<0.1% |
| Linear Shrinkage during UV-curing |
Internal Method |
0.5% |
0.5% |
| Linear Shrinkage during thermal cure |
Internal Method |
0.1% |
0.1% |
| Compression strength |
D695 |
155 MPa |
160 MPa |
| Density solid |
Internal Method |
1.62 g/cm3 |
1.62 g/cm3 |
Liquid Properties
| Description | ASTM Method |
|---|
| Appearance |
Opaque white liquid |
| Viscosity |
1400 cps at 25°C |
| Density |
1.52 g/cm3 |
| Ec |
9.55 mJ/cm2 |
| Dp metric |
0.18 mm |
| Dp imperial |
7.09 mils |